SCI论文中怎样描述TEM结果?

1. TEM详细描述样品有着怎样的形貌,由哪些微观结构组成。

实例一:Figure 1a shows a typical low-magnification transmission electron microscopy (TEM) image ofthe synthesized Co3O4,in which a batch of nanorodsis developed from a cluster core, forming a coral-like morphology.Most of the nanorods havestraight sides and regular ends,as shown in Fig. 1b, an enlarged TEM image.
(Ref.: Xie, X. et al.Nature,2009,458, 746-749)
句式模板:Figure _ shows a typical low-magnification transmission electron microscopy (TEM) image of the synthesized __, in which a batch of __ is developed from __, forming __ morphology. Most of the __ have __, as shown in Fig. _, an enlarged TEM image.
实例二:Atomic-resolution HAADF images ofthe gold particlesinthis sample reveal that they display a mixture ofcub-octahedral (Fig.2a), singly twinned (Fig. 2b) and multiply twinned (Fig. 2c)morphologies,with thetwinned variantsdominating.
(Ref.: Lopez-Sanchez,J. et al.Nat. Chem.2011, 3, 551-556)
句式模板:Atomic-resolution HAADF images of __ in this sample reveal that they display a mixture of __, __ and __ morphologies, with the __ dominating.
实例三:Transmission electron microscopy (TEM) studies reveal thatthe calcined BS-mTiO2possesses atwo-dimensional hexagonalmesophase.
(Ref.: Liu, X. et al.Chem. Commun.2010, 46, 6729-6731)
句式模板:Transmission electron microscopy (TEM) studies reveal that __ possesses a __ mesophase.
变型1The material has a __ mesostructure as determined by transmission electron microscopy (TEM).

变型2A typical TEM image, as presented in Figure _, indicates an __ with a diameter of about _ nm.
SCI论文中怎样描述TEM结果?
2. TEM结果描述样品的尺寸分布情况
实例一:A particle count taken from many such images, obtained from different regions of the sample,confirmed the presence of essentially monodispersedAuparticles of mean diameter1.4nm,which is the expected size ofAu55.
(Ref.:Turner, M. et al. Nature2008,454, 981-983)
句式模板:A particle count taken from many such images, obtained from different regions of the sample, confirmed the presence of essentially monodispersed __ particles of mean diameter _ nm, which is the expected size of __.
实例二:Transmission electron microscopy (TEM) analysis found that the metal NPs in thePt/SiO2(Fig. 3A) and Pt-Fe/SiO2(Fig. 3B)samplesare anchored evenly over thesilicahosts and have a narrow distribution in average size of2to3nm and2to4nm, respectively.
(Ref.: Fu,Q. et al.Science,2010, 328, 1141-1144)
句式模板:Transmission electron microscopy (TEM) analysis found that the metal NPs in the __ samples are anchored evenly over the __ hosts and have a narrow distribution in average size of _ to _ nm and _ to_ nm, respectively.
实例三:As can be seen fromFig. 1a,thePtPdNPsare well dispersed in them-SiO2framework and the sizes ofPtPd alloyNPs are rather small with a narrow size distribution(4.1±0.6nm).
(Ref.: Liu, J. et al.Catal. Sci. Technol.2014, 4, 441–446)
句式模板:As can be seen from Fig. _, the __ NPs are well dispersed in the __ framework and the sizes of __ NPs are rather small with a narrow size distribution (_ ± _ nm).
变型:In more detail, the enlarged TEM image in Fig. __ shows that the __ nanoparticlesare _ nm in size and densely and uniformly distributed in amorphous mesoporous__.(Ref.: Qiu, Y. et al.Chem. Commun.2010, 46,8359-8361)
SCI论文中怎样描述TEM结果?
3. HRTEM结果描述样品的晶格条纹等微观结构信息
实例一:High-resolution transmission electron microscopy (HRTEM) was used to characterize the catalysts after reaction (Figure 4).TheAu-0.0sampleshows the characteristic spacings of0.144and0.235nm for the(220)and the(111)lattice planes of FCCmetallic gold.TheAuCN-1.0sample (right panels) shows the expected spacings of0.306and0.312nm for the(012)and(101)lattice planes ofNa[Au(CN)2].
(Ref.: Oyama, S. et al.ChemCatChem2010, 2, 1582-1586)
句式模板:High-resolution transmission electronmicroscopy (HRTEM) was used to characterize the catalysts after reaction. The__ sample shows the characteristic spacings of _ and _ nm for the __ and the __lattice planes of FCC __. The __ sample shows the expected spacings of _ and _nm for the_and _lattice planes of __.
实例二:High-resolution TEM (HRTEM) images(Fig. 3, A and B, insets)show that NPs overboth Pt/SiO2and Pt-Fe/SiO2samples present the sameface-centered cubic ( FCC) Ptlattice with aPt(111)interlayer spacing of0.23nm.
(Ref. : Fu, Q. et al.Science,2010, 328, 1141-1144)
句式模板:High-resolution TEM (HRTEM) images show that NPs over __ samples present the same __ lattice with a __ interlayer spacing of _ nm.
实例三:As shown inFig. 1c,the lattice fringes ofPt1Pd3display interplanar spacings of0.223and0.192nm in the particle, which matchwell respectively with those of the(111)and the(200)planes of the fccPtPd alloy.
(Ref.: Liu, J. et al.Catal. Sci.Technol.2014, 4, 441–446)
句式模板:As shown in __, the lattice fringes of__ display interplanar spacings of _ and _ nm in the particle, which match well respectively with those of the __ and the __ planes of the fcc __.